HTB-1X
Carbon Steel Self-lubricating Bearing
To properly experience our LG.com website, you will need to use an alternate browser or upgrade to a newer version of internet Explorer (IE10 or greater).
LG.com utilizes responsive design to provide a convenient experience that conforms to your devices screen size. In order to get the best possible experience from our website, please follow below instructions.
If you’re using Internet Explorer 9 or earlier, you will need to use an alternate browser such as Firefox or Chrome or upgrade to a newer version of internet Explorer (IE10 or greater).
- Products
- Home
- About
- Our company is an entity enterprise specialized in manufacturing sliding bearing series products
- Product
- News
- Download
- We provide you with guaranteed quality products
- Technological
- Application
- Our company is an entity enterprise specialized in manufacturing sliding bearing series products
- Contact
HTB-702 Stainless Steel Base Point-lubricating Bearing
1/3
1/3
HTB-702 Stainless Steel Base Point-lubricating Bearing
HTB-702 Stainless Steel Base Point-lubricating Bearing
The product is made of high-quality stainless steel as the substrate, and the surface is sintered with lead bronze alloy. The solid lubricant is evenly distributed in the alloy layer. The surface of the alloy layer can be covered with a solid lubricating film according to actual needs. The product has a lower coefficient of friction and is better. The self-lubricating, wear-resistant and anti-seize properties are used in high loads, polluted environments and water or other liquids.
PRODUCT DATA
| Performance | Related data | |
|---|---|---|
| Maximum load pressure | Dead load | 200N/mm2 |
| Dynamic load | 80N/mm2 | |
| Maximum linear speed | 0.25 m/s | |
| Coefficient of friction | Dry | 0.13-0.18 |
| Oil | 0.11-0.16 | |
| Maximum PV value | 0.8N/mm2. m/s | |
| Temperature | -150oC~+280oC | |
| Linear expansion coefficient | 17.5×10-6/k | |
| Compressive strength | 320N/mm2 | |
| Density | 6.3g/cm2 | |
| Alloy hardness | ≥40HB | |